Hwm AISI 904L Super Austenitic Stainless Hlau

Manufacturing txheej txheem Excellence

Peb cov txheej txheem tsim khoom sib xyaw pib nrog lub tshuab nqus tsev induction melting siv cov khoom siv raw khoom, ua raws li electroslag remelting rau kev kho kom huv si. Kub dov yog ua nyob rau hauv qhov kub thiab txias ntau yam los txhim kho cov qauv nplej, thaum ua haujlwm txias ua kom tiav cov khoom siv kho qhov muag thiab qhov raug. Cov txheej txheem kho saum npoo av ua kom zoo tshaj plaws ua tiav thiab corrosion kuj.

🧪 Chemical Composition

Element	Kev sib xyaw (%)
Cov pa roj carbon (C)	Tsawg dua lossis sib npaug li 0.020
Manganese (Mn)	Tsawg dua lossis sib npaug li 2.00
Silicon (Si)	Tsawg dua lossis sib npaug li 1.00
Phosphorus (P)	Tsawg dua lossis sib npaug li 0.045
Sulfur (S)	Tsawg dua lossis sib npaug li 0.035
Chromium (Cr)	19.0 - 23.0
Nickel (Ni)	23.0 - 28.0
Molybdenum (hli)	4.0 - 5.0
Copper (Cu)	1.0 - 2.0
Nitrogen (N)	Tsawg dua lossis sib npaug li 0.10
Hlau (Fe)	Tshuav

⚙️ Mechanical Properties

Khoom	Tus nqi
Tensile zog (Rm)	Ntau dua lossis sib npaug li 490 MPa
Yield zog (Rp0.2)	Ntau dua lossis sib npaug li 220 MPa
Elongation (A5)	Ntau dua lossis sib npaug li 35%
Hardness (HB)	Tsawg dua los yog sib npaug li 250
Hardness (HV)	Tsawg dua lossis sib npaug li 270
Impact Zog (KV) ntawm 20 degree	Ntau dua lossis sib npaug li 100 J
Lub Modulus (E)	200 GPa
Shear Modulus (G)	81gp ua
Poisson tus ratio	0.27 - 0.30
Fatigue Limit (10 & sup7; cycles)	245 MPa rau