AISI 410 Stainless hlau nyob rau hauv Suav teb rau kev cai
Mar 23, 2026
Tso lus
🧪 Chemical Composition
| Lub ntsiab | Kev sib xyaw (%) |
|---|---|
| Cov pa roj carbon (C) | ≤ 0.15 |
| Manganese (Mn) | ≤ 1.00 |
| Silicon (Si) | ≤ 1.00 |
| Phosphorus (P) | ≤ 0.040 |
| Sulfur (S) | ≤ 0.030 |
| Chromium (Cr) | 11.5 - 13.5 |
| Nickel (Ni) | ≤ 0.75 |
| Hlau (Fe) | Tshuav |
⚙️ Mechanical Properties
| Khoom | Annealed mob | Hardened & Tempered |
|---|---|---|
| Tensile zog | 485-620 MPa | 725-850 MPa |
| Yield zog (0.2% offset) | 275-415 MPa | 550-690 MPa |
| Elongation (50 hli) | ≥ 20% | ≥ 15% |
| Kev txo qis ntawm cheeb tsam | ≥ 50% | ≥ 45% |
| Hardness (Brinell) | 155-217 HB | 235-285 HB |
| Hardness (Rockwell C) | - | 22-32 HRC |
| Impact Zog (Charpy V-notch) | 54-81 J | 27-54 J |
| Fatigue Limit (10 & sup7; cycles) | 240 MPa | 360 MPa |
🔬 Lub cev muaj zog
| Khoom | Tus nqi |
|---|---|
| Qhov ntom | 7.75 g / cm³ |
| Melting Point | 1480-1530 ° C |
| Thaum tshav kub kub (20 ° C) | 460 J/kg · K |
| Thermal conductivity (100 ° C) | 24.9 W/m·K |
| Thermal Expansion (20-100 ° C) | 9.9 × 10-6/K |
| Thermal Expansion (20-500 ° C) | 11.2 × 10-6/K |
| Hluav taws xob tiv taus (20 ° C) | 0.57 µm |
| Sib nqus Permeability | Ferromagnetic |
| Modulus ntawm Elasticity | 200 GPa |
| Poisson tus ratio | 0.27-0.30 |
📏 Product Specifications
| Yam khoom | Qhov Loj | Cov qauv |
|---|---|---|
| Round Bars | 6-300mm txoj kab uas hla | ASTM A276, A479 |
| Square Bars | 10-150 hli | ASTM A276, ASTM A276 |
| Pav ca Bars | 3-100mm tuab, mus txog 300mm dav | ASTM A276, ASTM A276 |
| Cov ntawv | 0.5-6mm tuab, mus txog 2000mm dav | ASTM A 240 Cov Lus Qhia |
| Daim phiaj | 6-100mm tuab, mus txog 3000mm dav | ASTM A 240 Cov Lus Qhia |
| Cov raj | 6-219mm OD, 0.5-20mm phab ntsa | ASTM A 268 Cov khoom siv |
| Nto tiav | Kub dov, txias kos, polished | 2B, BA, nr 4, nr 8 |
| Ua siab ntev | ± 0.1mm txog ± 1.0mm | EN 10029, ASTM A480 |