Corrosion Resistant 316L Stainless Hlau Sheet, Bar thiab Coil
Mar 16, 2026
Tso lus
Chemical Composition ntawm Stainless hlau 316
Table 1.Cov tshuaj muaj pes tsawg leeg rau 316 stainless hlau alloys
|
% |
316 |
316L |
316H |
316 Ti |
|
C |
0.0-0.07 |
0.0-0.03 |
0.04-0.08 |
0.0- 0.08 |
|
Mn |
0.0-2.0 |
0-2.0 |
0.0-2.00 |
0.0-2.00 |
|
Si |
0.0-1.0 |
0.0-1.00 |
0.0-1.00 |
0.0- 1.00 |
|
P |
0.0-0.05 |
0.0-0.05 |
0-0.04 |
0.0-0.05 |
|
S |
0.0-0.02 |
0.0-0.02 |
0.0-0.02 |
0.0-0.03 |
|
Cr |
16.50-18.50 |
16.50-18.50 |
16.50-18.50 |
16.50- 18.50 |
|
Mo |
2.00-2.50 |
2.00-2.50 |
2.00-2.50 |
2.00- 2.50 |
|
Ni |
10.00-13.00 |
10.00-13.00 |
10.00-13.00 |
10.50- 14.00 |
|
Ti |
- |
- |
- |
0.40- 0.70 |
|
Fe |
tshuav nyiaj li cas |
tshuav nyiaj li cas |
tshuav nyiaj li cas |
tshuav nyiaj li cas |
Cov khoom ntawm Stainless Hlau 316
Mechanical Properties ntawm Stainless Hlau 316
Rooj 2.Tej yam khoom siv rau 316 stainless hlau alloys
|
Qib |
316 Bar thiab Tshooj (txog 160 hli tuab) |
316 Sheet (txog 8 hli tuab) | 316 Phaj (8 - 75 hli tuab) | 316L Bar thiab Tshooj (txog 160 hli) |
316L Sheet (txog 8 hli tuab) |
316 L Phaj (8 - 75 hli tuab) |
316H Bar (txog 160 hli) |
316 TiB(txog 160 mm) |
|
Tensile zog (MPa) |
500 - 700 |
530 - 680 | 520 - 670 |
500 - 700 |
530 - 680 |
520 - 670 |
490 - 690 |
500 - 700 |
|
Pov thawj Stress (MPa) |
200 Min |
240 Min | 220 Min |
200 Min |
240 Min |
220 Min |
205 Min |
200 Min |
|
Elongation A50 hli |
40 Min % |
40 Min % |
45 Min % |
40 Min % |
40 Min % |
45 Min % |
35 % |
40 Min % |
|
Hardness Brinell |
215 Max HB |
- |
- |
215 Max HB |
- |
- |
- |
215 Max HB |