AISI 410 Martensitic Stainless hlau nyob hauv Suav teb
Mar 18, 2026
Tso lus
AISI 410 yog ib tug ncaj chromium martensitic stainless hlau nrog 11.5-13.5% chromium cov ntsiab lus, muab zoo heev corrosion kuj nyob rau hauv ib puag ncig me me. Martensitic microstructure tsim los ntawm kev tswj kom txias los ntawm austenitic kub, uas ua rau muaj zog thiab hardness muaj peev xwm.
Tshuaj muaj pes tsawg leeg
| Lub ntsiab | Kev sib xyaw (%) |
|---|---|
| Cov pa roj carbon (C) | ≤ 0.15 |
| Manganese (Mn) | ≤ 1.00 |
| Silicon (Si) | ≤ 1.00 |
| Phosphorus (P) | ≤ 0.040 |
| Sulfur (S) | ≤ 0.030 |
| Chromium (Cr) | 11.5 - 13.5 |
| Nickel (Ni) | ≤ 0.75 |
| Hlau (Fe) | Tshuav |
Mechanical Properties
| Khoom | Annealed mob | Hardened & Tempered |
|---|---|---|
| Tensile zog | 485-620 MPa | 725-850 MPa |
| Yield zog (0.2% offset) | 275-415 MPa | 550-690 MPa |
| Elongation (50 hli) | ≥ 20% | ≥ 15% |
| Kev txo qis ntawm cheeb tsam | ≥ 50% | ≥ 45% |
| Hardness (Brinell) | 155-217 HB | 235-285 HB |
| Hardness (Rockwell C) | - | 22-32 HRC |
| Impact Zog (Charpy V-notch) | 54-81 J | 27-54 J |
| Fatigue Limit (10 & sup7; cycles) | 240 MPa | 360 MPa |
Xa kev nug