316L Stainless hlau - Corrosion Resistant
Feb 26, 2026
Tso lus
Chemical Composition ntawm Stainless hlau 316
Table 1.Cov tshuaj muaj pes tsawg leeg rau 316 stainless hlau alloys
% | 316 | 316L | 316H | 316 Ti |
C | 0.0-0.07 | 0.0-0.03 | 0.04-0.08 | 0.0- 0.08 |
Mn | 0.0-2.0 | 0-2.0 | 0.0-2.00 | 0.0-2.00 |
Si | 0.0-1.0 | 0.0-1.00 | 0.0-1.00 | 0.0- 1.00 |
P | 0.0-0.05 | 0.0-0.05 | 0-0.04 | 0.0-0.05 |
S | 0.0-0.02 | 0.0-0.02 | 0.0-0.02 | 0.0-0.03 |
Cr | 16.50-18.50 | 16.50-18.50 | 16.50-18.50 | 16.50- 18.50 |
Mo | 2.00-2.50 | 2.00-2.50 | 2.00-2.50 | 2.00- 2.50 |
Ni | 10.00-13.00 | 10.00-13.00 | 10.00-13.00 | 10.50- 14.00 |
Ti | - | - | - | 0.40- 0.70 |
Fe | tshuav nyiaj li cas | tshuav nyiaj li cas | tshuav nyiaj li cas | tshuav nyiaj li cas |
Cov khoom ntawm Stainless Hlau 316
Mechanical Properties ntawm Stainless Hlau 316
Rooj 2.Tej yam khoom siv rau 316 stainless hlau alloys
Qib | 316 Bar thiab Tshooj (txog 160 hli tuab) | 316 Sheet (txog 8 hli tuab) | 316 Phaj (8 - 75 hli tuab) | 316L Bar thiab Tshooj (txog 160 hli) | 316L Sheet (txog 8 hli tuab) | 316 L Phaj (8 - 75 hli tuab) | 316H Bar (txog 160 hli) | 316 TiB(txog 160 mm) |
Tensile zog (MPa) | 500 - 700 | 530 - 680 | 520 - 670 | 500 - 700 | 530 - 680 | 520 - 670 | 490 - 690 | 500 - 700 |
Pov thawj Stress (MPa) | 200 Min | 240 Min | 220 Min | 200 Min | 240 Min | 220 Min | 205 Min | 200 Min |
Elongation A50 hli | 40 Min % | 40 Min % | 45 Min % | 40 Min % | 40 Min % | 45 Min % | 35 % | 40 Min % |
Hardness Brinell | 215 Max HB | - | - | 215 Max HB | - | - | - | 215 Max HB |