Hwm AISI 310S Austenitic Stainless Hlau hauv Suav teb
Mar 18, 2026
Tso lus
Tshuaj muaj pes tsawg leeg
| Element | Kev sib xyaw (%) |
|---|---|
| Cov pa roj carbon (C) | ≤ 0.08 |
| Manganese (Mn) | ≤ 2.00 |
| Silicon (Si) | ≤ 1.50 |
| Phosphorus (P) | ≤ 0.045 |
| Sulfur (S) | ≤ 0.030 |
| Chromium (Cr) | 24.0 - 26.0 |
| Nickel (Ni) | 19.0 - 22.0 |
| Nitrogen (N) | ≤ 0.10 |
| Hlau (Fe) | Tshuav |
⚙️ Mechanical Properties
| Khoom | Tus nqi |
|---|---|
| Tensile Strength (Chav Kub) | ≥515 MPa |
| Yield zog (0.2% Offset) | ≥205 MPa |
| Elongation (50 hli ntsuas) | ≥ 40% |
| Hardness (Brinell) | ≤ 217 HB |
| Hardness (Rockwell B) | ≤ 95 HRB |
| Impact Zog (Charpy V-notch) | ≥ 120 J |
| Young's Modulus | 200 GPa |
| Fatigue Limit (107lub voj voog) | 240 MPa |
🔬 Lub cev muaj zog
| Khoom | Tus nqi |
|---|---|
| Qhov ntom | 7,98 g/m² |
| Melting Point | 1400-1450 ° C |
| Thermal conductivity (20 ° C) | 14.2 W/m·K |
| Thermal Expansion Coefficient (20-100 ° C) | 14.4 × 10-6/K |
| Thermal Expansion Coefficient (20-1000 ° C) | 18.0 × 10-6/K |
| Tshwj xeeb kub muaj peev xwm | 500 J/kg · K |
| Hluav taws xob tiv taus (20 ° C) | 0,78m ;ua |
| Sib nqus Permeability | 1.02 µH/m (Tsis yog-magnetic) |
| Poisson tus ratio | 0.27-0.30 |