430 Stainless Hlau Ntawv Nyiaj Qib

 

Chemical Composition ntawm Stainless hlau 430

Table 1.Cov tshuaj muaj pes tsawg leeg rau 430 stainless hlau alloys

%	430
C	0-0.08
Mn	0-1.00
Si	0-1.00
P	0-0.04
S	0-0.02
Cr	16-18
Fe	Tshuav

 

Cov khoom ntawm Stainless hlau 430

Mechanical Properties ntawm Stainless hlau 430

Rooj 2.Mechanical zog ntawm 430 stainless hlau alloys

Khoom	Sheet (txog 8 hli tuab)	Phaj (8 - 13.5 hli tuab)	Phaj (13.5 - 25 hli tuab)	Bar (txog 100 mm inch)
Tensile zog (MPa)	450 - 600 MPa	450 - 600 MPa	430 - 630 MPa	400 - 630 MPa
Pov thawj Stress 0.2% (MPa)	260 Min MPa	240 Min MPa	240 Min MPa	240 Min MPa
Elongation (%)	20 Min %	18 Min %	20 Min %	20 Min %

Lub cev muaj zog ntawm Stainless hlau 430

Table 3.Lub cev muaj zog ntawm 430 stainless hlau alloys

Khoom	Tus nqi
Qhov ntom	7.75 g / cm33
Melting Point	1425-1510 ° C
Modulus ntawm Elasticity	200 GPa
Hluav taws xob Resistivity	0.60 x 10-6Ω.m
Thermal conductivity	23.9 W / mK ntawm 100 ° C
Thermal Expansion	10.4 x 10-6/ K ntawm 100 ° C